Comprehensive
range of insulation material, specially developed to meet high
temperature, fire resistance and electrical insulation
requirement of various industries.
Silicone
Elastomer Glass Tape
This Tape has excellent flexibility of
Silicone Elastomer and strength of Fiber glass fabric .It retains high
dielectric strength over a wide temperature range 40 °C to 260 °C.
It has good humidity barrier, resists are tracking and corona resistance.
Suitable for application where high starting loads and greater switching
frequency is required.
Typical Properties:
 |
| Thickness
(mm) |
0.15 |
0.18 |
0.25 |
| Tolerance
(mm) |
± 0.015 |
± 0.02 |
± 0.02 |
| Width |
As per requirement |
As per requirement |
As per requirement |
| Tensile
Strength (Kg/Cm) |
8 |
8 |
12 |
| BDV
(KV) |
4.5 |
6 |
7.5 |
| Water
Absorption (Max.) |
1% |
1% |
1% |
| Volume
Resistivity (Ohm.Cm) |
6 x 10 12 |
6 x 10 12 |
6 x 10 12 |
| Class
Of Insulation |
H |
H |
H |
| Crease
Resistance |
Excellent |
Excellent |
Excellent |
| TEST
METHOD : |
IEC 60394.2 |
|
|
Self Fusing Silicone Rubber Tape
Self fusing silicone rubber tape is
suitable for field insulation, bus-bar insulation & in splicing and
termination of cables. It is designed to withstand high temperature, this
cost effective product is available in the given sizes:
Typical Properties:
|
| Test |
Grade 4360 |
| Thickness
(mm) |
0.25 , 0.38 , 0.50 , 1.00 MM ( ±
0.03 ) |
| Width
(mm) |
± 1.5 MM |
| Tensile
Strength Breaking Load Kg/Cm 2 |
45 |
| Elongation% |
300 % MIN |
| Electrical
Strength (Kv/mm) |
20 |
| VOLUME
RESISTIVITY OHM.CM |
3 X 1014 |
| Water
Absorption |
1 % MAX |
| SELF BONDING
PROPERTY (42 MM OVERLAP, 2KG LOAD 15MIN) |
Excellent |
| Thermal
Resistance |
200 CLASS |
|
|
Silicone
Cable
We, through our advanced technology and
absolute engineering, manufacture and export superior quality silicone
cable. Our silicone cable has been serving in many industries with utmost
perfection. Our silicone cable is ozone, flame & heat resistant, which
enables them to work efficiently in their specified application in ovens,
electric motors, dryers, ballasts, transformers, locomotives, electronic
devices, therapeutic devices and other applications.
Typical Properties:
|
| Standard
Sizes |
0.50, 0.75,1.00, 1.5, 2.5, 4.0,
6.0, 10,16,25 SQ MM |
| Electrical
Strength |
600 VOLTS |
| Conductor
Temp |
200 C MAX NORMAL , 350 C SHORT CIRCUIT |
| Ozone
Resistance |
Good |
| Flame
Resistance |
Good |
| Moisture
Resistance |
Excellent |
| Flexibility |
Good |
|
|
|
| Area In Sq Mm |
Conductor
Construction |
Bunched
Conductor Size Mm |
Max
res. Ohm/km |
Insulation
Thk mm |
OD |
Current
Rating Amp |
| 0.50 |
16 X 0.2 MM |
0.94 |
39 |
0.6 |
2.2 |
4.0 |
| 0.75 |
24 X 0.2 MM |
1.2 |
26 |
0.6 |
2.5 |
7.0 |
| 1.0 |
32 X 0.2 MM |
1.34 |
19.5 |
0.6 |
2.6 |
11.0 |
| 1.5 |
48 X 0.2 MM |
1.64 |
13.3 |
0.6 |
2.9 |
14.0 |
| 2.5 |
50 X 0.25 MM |
2.08 |
7.98 |
0.7 |
3.5 |
19.0 |
| 4.0 |
56 X 0.30 M |
2.61 |
4.95 |
0.8 |
4.3 |
26.0 |
| 6.0 |
64 X 0.30 MM |
3.5 |
3.013 |
1.0 |
5.6 |
31.0 |
| 10 |
80 X 0.40 MM |
4.6 |
1.86 |
1.0 |
6.7 |
42.0 |
| 16 |
124 X 0.4 MM |
5.9 |
1.15 |
1.2 |
804 |
57.0 |
| 25 |
200 X 0.45 MM |
9.6 |
0.691 |
1.4 |
9.5 |
57.0 |
|
|
Silicone
Glass Sleeve
Extremely flexible giving high dielectric
protection at continuous temp 180 C. Good abrasion resistance & fire
retardancy. Used for covering live wires, lead wires in ship. aerospace
railway & electronics.
Typical Properties:
|
| Grade |
433D |
433C |
433B |
433A |
| Wall Thickness |
0.4mm |
0.5mm |
0.7mm |
0.9mm |
| Tolerance |
±0.1mm |
±0.1mm |
±0.15mm |
±0.15mm |
| Bore ID |
1-25mm |
1-25mm |
1-25mm |
1-25mm |
| Voltage Proof Test at RT in Air 1 Min |
600V |
3KV |
5KV |
7KV |
| Voltage Proof Test at 200 C Air 1 Min |
600V |
3KV |
5KV |
7KV |
| Voltage Proof at R T in Water 1 Min |
NA |
2.5 KV |
4 KV |
5.5 KV |
| Thermal Class |
180 |
180 |
180 |
180 |
| Bending after Heat Aging 200 C |
No sign of crack, detachment or
delamination |
| Self extinguishing test |
Maximum 60 seconds |
| Fire Retardancy |
On request V-0, V-1 or V-2 as per
UL 94 Method |
|
|
Silicone Polyester Films
We offer quality silicon polyester film
that offers excellent release property. Superior in quality, this product
can be used as moulds release tape during molding of class 'F' high -
voltage coils.
Typical Properties:
|
| Base |
1181 |
| Base |
Polyester Film |
| Thickness |
0.05 ± 0.01 MM |
| Width |
25 ± 1 MM |
| Breaking Load |
12 KG/25 mm Min |
| Elongation |
50 % Min |
| Thermal Shrinkage at
180°C - 30 min |
6 % max |
| Coating |
Silicone release compound on both
sides |
| Test Method |
IEC 60674.2 |
|
|
© 3A Associates Incorporated. All Rights Reserved (Terms of Use)